€189,80 EUR €272,90 EUR VAT Excluded
SKU 50060
Normally available in 6/10g
Aliquota IVA applicata: 22%
Ideal alloy for frameworks for combined prostheses. With a higher yield strength and tensile strength, this alloy is harder and more rigid: ideal for combined prostheses.
Technical characteristics:
Mass composition -% Co 63 - Cr 30 - Mo 5 - Si 1.1 - Mn <1 - C <1 -
Density [g/m³): 8.2
Preheating temperature [°C]: 950 - 1050
Pouring temperature [°C]: approx. 1420
Melting range [°C]: 1260 - 1305
Elastic modulus [GPa]: approx. 225
Yield strength [RP 0.2] after melting/firing: 625
Yield strength [RP 0.2] quenched: 625
Tensile strength [RM]: 910
Elongation at break [A5] after sintering/firing: 4.1
Vickers hardness [HV10] after sintering/firing: 375